Pengujian Puntir Poros Komposit Serat Gelas Berlapis Simetri Dengan Lapisan Bersudut ( Angle Ply) Torsion Testing Of symetrical Anegel Ply Laminated Glass/ Epoxy Composite Shaft
|Pengarang||:||Heru Santoso B. Rochardjo' dan Edi Wiyanto2|
|Jurnal||:||Jurnal Mesin dan Industri 2004, I(3)|
|Summary / Kata Kunci||:||Glass/epoxy composite shafts were tested under torsion loading. The material which was made by filament winding method is simetric angle-ply laminate with 4 plies. The fiber orientations q, were varied from 15 degrees to 75 degrees to the tube axis, to make laminated composite with [q,-q]3structure. It was shown from the experimental result, that the shear strength of the shaft is agree better with Tsai-Hill failure criteria than with the maximum stress criteria. The shear stiffness, however, is below the calculated value.
Keywords: glass/epoxy, composite, filament winding, laminate.
|(tidak ada sitasi)|
|1.||About Wafa M. N., Hamdi, A. and El Midany,, "Combined Bending and Torsional Fatigue of Woven Roving GRP, 1977|
|2.||Billmeye Fred W., "Text Book of Polymer Science",, 1994|
|3.||E. D. Harmer , G. E. Troxell and George F. W. H.,, "The Testing of Engineering Materials",, 1964|
|4.||F. R. Gibson ,, "Principle of Composit Materials Mechanics",, 1994|
|5.||G. H.Dietz A. ,, "Composite Material Hand Book",, 1978|
|6.||G.R.Budynas ,, "Advanced Strength and applied Stess Analysis",, 1977|
|7.||R. Jones M., Mechanic of Composite Materi, 1975|