KARAKTERISASI SAMBUNGAN ADESIF PADA PELAT PADUAN ALUMINIUM 2024 - T3 (ADHESIVE - BONDED JOINTS CHARACTERIZATION ON ALUMINUM ALLOY 2024 - T3)
Pengarang : Yusep Mujalis, Purnomo, Victor Malau
Jurnal : Teknosains 2001, XIV(2)
Tahun : 2001
Summary / Kata Kunci : ABSTRACT
The objective of this research was to determine the characteristics of adhesive-bonded joints of Aluminum alloy 2024 - T3 with mode I. The characteristics included the shear strength, critical strain energy release rate, compliance, and crack propagation.
Adherends used in this research were aluminum 2024 - T3 plates in double-cantilever beam of 135x25x2 mm. The adhesive materials were Plastic Steel Epoxy, White 2 Ton Epoxy, Epikol Adhesive Epoxy, and Epoxy Resin. The materials for etching were hydrochloric and nitrioacids solutions with 1 : 1 compositions. Materials and instruments used, were solution for making surface roughness and surface roughness tester, heater for specimen curing, and tensile tester.
The results 'showed that the greatest shear strenght was indicated by Epoxy Resin adhesive (t=13.692 MPa). The greatest rate of critical strain energy release was shown by Epoxy Resin adhesive (Gig = 1297.061 J/ m2). The greatest compliance was indicated by Plastic Steel Epoxy adhesive (C = 0.4303 mm/N), the greatest crack propagation was demonstrated by Plastic Steel Epoxy adhesive (Da = 85 mm ).

Key words : Adhesive bonded-joints, strain energy release rate, crack propagation, compliance, displacement.
File : Login Required
     
Sitasi  
    (tidak ada sitasi)
     
Referensi    
1.   D. Broek, " Elementary Engineering Fracture Mechanic ", Martinus Nijhoff Publishers, Boston., 1987
2.   D.J. Wilkins, J.R. Eissenmann, R.A. Curtin, W.S. Margolis, R.A. Benson, " Characterizing Delamination Growth in Graphite-Epoxy Damage in Composite Material, ASTM Si'? 775, K. L. Reif snider, Ed., American Societ, 1982
3.   G. Marom, I. Roman, H. Harel, Rosensaft, The Characterization of Mode I and Mode II Delamination Failures in Fabric-Reinforced Laminates", Graduate School of Applied Science and Technology ", the Hebrew University of Jerusalem, pp, 3265-3273, Israel., -
4.   L. Tong, A. Sheppard, D. Kelly, Relation Between Surface and Adhesive Peel Stress in Bonded Double Lap Joints ",Int.J.Adhesion and Adhesives,15, 43-48., 1995
5.   P. Krawczak, J. Pabiot,, Fracture Mechanics Applied to Glass Fibre/Epoxy Matrix Interface Characterization ", Journal of Composite Materials, 29 (17), 7730-2253., 1995
6.   S. C. Pradhan, N. G. R Iyerngar, N. N. Kishore, " Finite Element Analysis of Crack Growth in Adhesively Bonded Joints ",Int.J.Adhesion and Adhesives,15, 33-41., 1995
7.   Y. Baziard, R.E. Abdi, D Amara, J.A. Petit, " Study of Critical Failure Parameters for an Adhesive-Bonded Single Lap Joint with Ceramic Adherens ", Int.J.Adhesion and Adhesives, 15, 155-160., 1995
     
     
Inherent UGM
Gedung Pusat UGM
Lt 3 Sayap Utara
Bulaksumur
Telp. (0274) 564416